EN 1.0038 Steel S235JR Material Equivalent, Properties, Composition


S235JR Material Introduction现货价格查询

EN 10025 S235JR material (1.0038 steel) is an European standard hot rolled non-alloy structural steel grade. It has good plasticity, toughness and weldability, certain strength and good cold bending properties. For specification, datasheet and equivalent, please see the following tables.

Material S235JR meaning (designation):

  • “S” is short for structural steel;
  • “235” refers to the minimum yield strength (MPa) for the steel thickness ≤ 16mm;
  • “JR” indicates the quality grade related to charpy impact test energy value ≥ 27 J, at room temperature 20℃;
  • “C” means the material is suitable for cold flanging, cold bending, cold forming or cold drawing, e.g. S235JRC (1.0122).
  • 1.0038 is the steel number of this steel.

Carbon steel S235JR general delivery conditions are as follows:

  • +AR means “as-rolled” and delivery condition without special rolling and/or heat treatment.
  • +N stands for “normalized or normalized formed”
  • +M refers to “thermomechanically formed – TMCP”
  • +C is the “cold work hardened”
  • +A means that the mateiral is in the soft annealed condition.
  • +AT means that the steel is in the solution annealed condition.

Example 1: When the delivery condition is as-rolled or normalized, the steel name is given as S235JR+AR (1.0038+AR) or S235JR+N (1.0038+N).

Example 2: S235JRC steel means the material is suitable for cold flanging, cold bending, cold forming or cold drawing.

Example 3: If S235JRC steel is delivered in the condition of cold work hardened, it’s named as S235JRC+C (1.0122+C).

Material 1.0038 Datasheet & Specification

The following tables and lists show S235JR datasheet and specification including chemical composition, mechanical properties and physical properties, etc. The data sheet of DIN EN 10025-2 is the same as BS EN 10025-2 and other EU member states’.

Chemical Composition of S235JR Material (EN 1.0038 Steel)

The following table shows (1.0038) S235JR chemical composition based on ladle analysis.

      Chemical Composition (ladle analysis) %, ≤
Standard Grade Steel Grade (Steel Number) C Si Mn P S Cu N
EN 10025-2 S235 steel S235JR (1.0038) 0.17 – 1.40 0.035 0.035 0.55 0.012
S235J0 (1.0114) 0.17 – 1.40 0.030 0.030 0.55 0.012
S235J2 (1.0117) 0.17 – 1.40 0.025 0.025 0.55 –

Physical Properties of S235JR Steel (1.0038 Material)

  • Material density: 7.85g/cm3
  • Melting point: 1420-1460 °C (2590-2660 °F)

S235JR Steel (1.0038 Material) Mechanical Properties

The yield strength, tensile strength, elongation, and Charpy impact test are listed in the following data sheet.

  • EN 1.0038 material Brinell hardness: ≤120 HBW
  • Charpy impact value: ≥ 27J, at room temperature 20 ℃.

Yield Strength

    Yield Strength (≥ N/mm2); Dia. (d) mm
Steel Series Steel Grade (Material Number) d≤16 16< d ≤40 40< d ≤100 100< d ≤150 150< d ≤200 200< d ≤250
S235 S235JR (1.0038) 235 225 215 195 185 175

Tensile Strength

    Tensile Strength (≥ N/mm2)
Steel Series Steel Grade (Material Number) d<3 3 ≤ d ≤ 100 100 < d ≤ 150 150 < d ≤ 250
S235 S235JR (1.0038) 360-510 360-510 350-500 340-490

1MPa = 1N/mm2

Elongation

    Elongation (≥%); Thickness (d) mm
Steel Series Steel Grade 3≤ d≤40 40< d ≤63 63< d ≤100 100 < d ≤ 150 150 < d ≤ 250
S235 S235JR 26 25 24 22 21

Applications

EN 1.0038 material can be made into many steel products, such as H beam, I beam, steel channel, steel plate, steel angle, steel pipe, wire rods, and nails, etc. and these products are widely used in general requirements for welded structures and parts such as bridges, transmission towers, boilers, steel structure factories, shopping centers and other buildings, etc.

Equivalent Grade

EN 1.0038 material S235JRG2 or S235JR steel equivalent to US ASTM AISI SAE, European EN (German DIN, British BSI, France NF…), ISO, Japanese JIS, Chinese GB, and Indian standard. (For reference)

Notes: S235JRG2 is the former designation, and has been discarded and covered by S235JR in EN 10025-2 since 2004.

EN 1.0038, S235JR steel equivalent grade
European Union US Germany Japan China India ISO
Standard Steel name (Stee number) Standard Grade Standard Steel name Standard Grade Standard Grade Standard Grade Standard Grade
EN 10025-2 S235JR (1.0038);
S235JRG2		 ASTM A36;
ASTM A283/A283M		 A36;
Grade D		 DIN 17100 St37, RSt 37-2, Ust 37-2 JIS G3101;
JIS G3106		 SS400;
SM400A		 GB/T 700 Q235B, Q235C IS 2062 E250A ISO 630-2 S235B
EN 10025-2 S235J0 (1.0114) ASTM A36;
ASTM A283/A238M;
ASTM A573/A573M		 A36;
Grade D
Grade 58		 DIN 17100 St 37-3 U JIS G3106 SM400A,
SM400B		 GB/T 700 Q235C;
Q235D		 IS 2062 E250 ISO 630-2 S235C
EN 10025-2 S235J2 (1.0114);
S235J2G3;
S235J2G4		 ASTM A36;
ASTM A283M		 A36;
Grade D		     JIS G3106 SM400A GB/T 700 Q235D IS 2062 E250 ISO 630-2 S235D

EN 10025 S355 Steel
16MnCr5 (1.7131)